Technical Sheet III
SPEC.ASTM | A312 | A335 | A350 | |||||||||||||||
GRADE | TP304 | TP304H | TP304L | TP316 | TP316H | TP316L | TP321 | TP321H | TP347 | TP347H | P5 | P9 | P11 | P22 | LF2 | LF3 | ||
C | min | 0.08 | 0.04 | 0.035 | 0.08 | 0.04 | 0.035 | 0.08 | 0.04 | 0.08 | 0.04 | 0.15 | 0.15 | 0.05 | 0.05 | 0.35 | 0.2 | |
max | 0.1 | 0.1 | 0.1 | 0.1 | 0.15 | 0.15 | ||||||||||||
Mn | min | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 0.3 | 0.3 | 0.3 | 0.3 | 0.6 | ||
max | 0.6 | 0.6 | 0.6 | 0.6 | 1.35 | 0.9 | ||||||||||||
P | max | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.025 | 0.025 | 0.025 | 0.025 | 0.035 | 0.035 | |
S | max | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.025 | 0.025 | 0.025 | 0.025 | 0.04 | 0.04 | |
Si | min | 0.25 | 0.5 | 0.15 | 0.2 | |||||||||||||
max | 0.75 | 0.75 | 0.75 | 0.75 | 0.75 | 0.75 | 0.75 | 0.75 | 0.75 | 0.75 | 0.5 | 1 | 1 | 0.5 | 0.3 | 0.3 | ||
Cu | max | 0.40 B | 0.40 c | |||||||||||||||
NI | min | 8 | 8 | 8 | 11 | 11 | 10 | 9 | 9 | 9 | 9 | 0.40 B | 3.3 | |||||
max | 11 | 11 | 13 | 14 | 14 | 15 | 13 | 13 | 13 | 13 | 3.7 | |||||||
Cr | min | 18 | 18 | 18 | 16 | 16 | 16 | 17 | 17 | 17 | 17 | 4 | 8 | 1 | 1.9 | |||
max | 20 | 20 | 20 | 18 | 18 | 18 | 20 | 20 | 20 | 20 | 6 | 10 | 1.5 | 2.6 | 0.3 Bc | 0.3 c | ||
Mo | min | 2 | 2 | 2 | 0.45 | 0.9 | 0.44 | 0.87 | ||||||||||
max | 3 | 3 | 3 | 0.5 | 1.1 | 0.65 | 1.13 | 0.12 Bc | 0.12 c | |||||||||
Nb | max | 0.02 | 0.02 | |||||||||||||||
AL | ||||||||||||||||||
Ti | ||||||||||||||||||
Bo | ||||||||||||||||||
V | max | 0.05 | 0.03 | |||||||||||||||
Tensile strength min. | PSI x 1k | 75 | 75 | 70 | 75 | 75 | 70 | 75 | 75 | 75 | 75 | 60 | 60 | 60 | 60 | 70- 95 | 70- 95 | |
MPA | 515 | 515 | 485 | 515 | 515 | 485 | 515 | 515 | 515 | 515 | 415 | 415 | 415 | 415 | 485- 655 | 485- 655 | ||
Yeld strength min. | PSI x 1k | 30 | 30 | 25 | 30 | 30 | 25 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 36 | 37.5 | |
MPA | 205 | 205 | 170 | 205 | 205 | 170 | 205 | 205 | 205 | 205 | 205 | 205 | 205 | 205 | 250 | 260 | ||
Elongation in 2 in. Min. 2% | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 35 | 22 | 22 | 22 | 22 | 22 | 22 | ||
30 | 35 | |||||||||||||||||
Hardness test HB. | min | |||||||||||||||||
max |
(B):the sum of copper, nickel, chromium and molybdenum shall not exceed 1.00% on heat analysis
(C): the sum of chromium and molybdenum shall not exceed 0.32% on heat analysis.